Implementatienormen: GB/T8162 naadloze stalen buis voor structuur, GB/T8163 naadloze stalen buis voor vloeistoftransport. 0420D en 0420E mechanische eigenschappen: treksterkte 520 ~ 680 MPa,<16 service strength 2420MPa, 16mm~30mm service strength 2400, 230mm Yield strength 2380MPa Impact test Q420D minus 20C Impact energy 234, impact test Q420E minus 40C Impact energy 227 :0.20, chromium: <0.30, nickel: <0.50, copper: 0.20, nitrogen: 0.015, :0.20, aluminum, 20.015.Q420E seamless steel pipe chemical composition: carbon: 0.20, silicon: 0.50, :1.70, phosphorus: 0.025, Sulfur: 0.020, : 0.07, : 0.20, : 0.20 Chromium: <0.30, Nickel: <0.50, Copper: <0.20, Nitrogen: 0.015, : 0.20, Aluminum, 20.015. Steel refining method: Steel should be processed by electric arc furnace Refining outside the furnace or gas converter plus outside refining method. After negotiation between the supply and demand parties, other methods with higher requirements can also be used to treat refining. When the demander requires a certain refining method, it should be stated in the contract.
Productiemethode voor buizen: Buizen kunnen ook worden vervaardigd door continugieten, vormgieten of warmwalsen.
Continu gegoten buizen moeten ook voldoen aan de voorschriften van YB/T 4149; hete leidingen moeten ook voldoen aan de voorschriften van YB/T 5221 of YB/T 5222; gegoten buizen kunnen ook verwijzen naar de voorschriften voor hete (gesmede) buizen.