Rare earth has a strong chemical affinity with impurities such as oxygen and sulfur in molten steel. At steelmaking temperature (about 1873K), rare earth can react with impurities such as oxygen and sulfur in molten steel to form rare earth oxides, sulfides or oxysulfides. The deoxidation equilibrium constant or desulfurization equilibrium constant of these reactions is lower than or close to that of commonly used deoxidizers and desulfurizers. Therefore, rare earth steel additives can be used as strong deoxidizers and desulfurizers for molten steel to purify it. Commonly used rare earth steel additives are mainly mixed rare earth metals or high-grade (RE>27%) Er worden ook ferrosiliciumlegeringen van zeldzame aardmetalen en soms zeldzame aardoxides met gemengde reductiemiddelen gebruikt.
Oxiden, sulfiden of oxysulfiden die worden gegenereerd door de reactie van zeldzame aardmetalen met zuurstof en zwavel in gesmolten staal kunnen gedeeltelijk in het gesmolten staal achterblijven en insluitsels in het staal worden. Vanwege het hoge smeltpunt van deze insluitsels kunnen ze dienen als inhomogene kernvormingscentra wanneer het gesmolten staal stolt, en een rol spelen bij het verfijnen van de stollingsstructuur van het staal; en omdat deze insluitsels niet gemakkelijk worden vervormd bij de walstemperatuur, behouden ze nog steeds een kleine bolvormige of spilvorm, zodat de morfologie van insluitsels in het staal kan worden gecontroleerd, waardoor de anisotropie van staaleigenschappen, veroorzaakt door de verlenging en overwonnen wordt, wordt vermeden of overwonnen. vervorming van andere soorten insluitsels (zoals MnS) tijdens verwerking onder warme druk, en het consistent maken van de longitudinale, transversale en dikterichtingen van de staaleigenschappen. Dit soort modificatie van met zeldzame aardmetalen behandeld staal is momenteel de belangrijkste toepassingsinhoud van additieven voor zeldzame aardstaal.